Art Clay Silver 650 |
Art Clay Silver (original) |
Silver Contents |
92% (clay type) *clay type only |
92% (clay type), 80% (paste type), 87%
(syringe type)
|
Available Size |
7g, 10g and 20g |
5g, 7g, 10g, 20g, 50g and 100g |
Container |
Aluminum bag w/ zip-lock *Able to
preserve unused clay portion in the bag |
Aluminum pack in a paper box *Need
airtight container to preserve unused clay portion. |
Composition |
Pure Silver particle, binding agent and
water. The binding agent is produced from harmless pulp fiber |
Same as 650 |
Contraction |
8-9% |
10-12% |
Drying Time |
Hair Dryer
(1200w) At least 10-15 minutes 10cm/4 inches from the piece |
Hair Dryer (1200w) - Same as 650 |
|
Cooking Plate
At least 7-10 minutes at 150 degrees C-180 degrees C/ 300-330
degrees F |
Cooking plate - Same as 650 |
|
Electric Kiln At least 7-10 minutes at 150 degrees
C/300 degrees F |
Electric Kiln - Same as 650 |
|
Natural Dry At least 24 hours at room temperature |
Natural Dry - Same as 650 |
Firing Temperature and Holding Time |
650 degrees C/1200 degrees F - hold time 30 minutes |
800 degrees C/1470 degrees F - hold time 30 minutes |
|
700 degrees C/1290 degrees F - hold time 15 minutes |
850 degrees C/1560 degrees F - hold time 20 minutes |
|
750 degrees C/1380 degress F - hold time 10 minutes |
870 degrees C/1600 degrees F - hold time 10 minutes |
|
780 degrees C/1435 degrees F and above - hold time 5 minutes
|
------------------ |
Firing Methods |
Electric kiln, Butane gas torch and Gas operated cooking stove
|
Same as 650 |
Other Features |
Able to fire SV925 findings along. *Firing at 650 degrees C/1200
degrees F and use of quality of SV925 and up are recommended
|
Not recommended |
|
Because of the low firing, it broadens your choice of combining
with a variety of glazed objects, such as glass, ceremic and porcelain.
|
Limits your choice of combining with a variety of glazed objects
|
|
Fired object has slightly more bluish silver brightness after polishing compare
to the Original |
Fired objects has silver brightness after polishing |
|
Has very stable contraction ratio in different temperatures |
Has slightly different contraction ratio depends on the firing temperatures
|